WELDING THE SOLID STATE OF Zn-22 % Al ALLOY UNDER IN LOW-TEMPERATURE SUPERPLASTICITY CONDITIONS

10.25712/ASTU.1811-1416.2023.02.012

Abstract

The new approach to solid state pressure welding of aluminum-zinc alloy Zn-22 % Al in vacuum at a temperature of 250 °C under conditions of low-temperature superplasticity is proposed. An ultrafine equiaxial structure with an average size of both phases was obtained by annealing in an oven at 350 °C followed by quenching in water. This treatment produces stable ultrafine grains of about 0.65 μm with a uniform distribution of Zn and Al grains. When welding high-height billets with pressure, barrel-like properties appear on the side surface of welded materials. It is shown that the sizing of the mold for pressure welding of cylindrical billets makes it possible to influence development of local flow and to provide the most favorable conditions of deformation by optimizing energy consumption for deformation in zone of welded joint. As a result of heating and precipitation, a joint superplastic deformation occurs and the main deformation is localized in the region of formation of the solid-phase joint, while most of the blanks are slightly deformed. Oxide films on the surfaces to be joined are broken by extrusion and removed by superplastic deformation in radial directions and a new oxide-free layer appears on the surface of the workpieces to be welded. The welded is formed due to the occurrence of metal bonds between the juvenile contacting surfaces of the welded workpieces. Mechanical tensile tests showed that the strength of the solid phase joints was 90-95% of the ultimate strength of the base material.