FEATURES OF THE STRUCTURE OF THIN 20GL STEEL SAMPLES OBTAINED BY CASTING GASIFIED PATTERNS TECHNOLOGY
EDN: LBSKMM
DOI:
https://doi.org/10.25712/ASTU.2072-8921.2022.02.019Keywords:
steel, casting, casting according to gasified models, microstructure, liquation, carbon.Abstract
The work is devoted to the study of carbon liquation in cast steel samples with a thickness of 8 mm obtained by a special method of casting according to gasified models (LGM). In the course of the work, steel castings with a thickness of 8 mm were obtained. The microstructure of castings was studied both before heat treatment and after TO (annealing). Studies have shown that in the process of pouring metal during the destruction of expanded polystyrene, intensive carburization of steel occurs not only in the surface area, but also throughout the cross-section of the samples. Traditional heat treatment of steel castings (annealing) does not have a significant effect on the redistribution of carbon in the volume of the casting, that is, it does not reduce the carbon liquation along the sample cross-section.
References
Шуляк В.С. Литье по газифицируемым моделям. СПб. : Изд-во НПО «Профессионал», 2007. 408 с.
Озеров В.А., Шуляк В.С., Плотников Г.А. Литье по моделям из пенополистирола. М., «Машиностроение», 1970. 183 с.
Шуляк В.С. О состоянии и развитии производства отливок литьем по газифицируемым моделям в России // Сб. трудов 1-й Международной научно-практической конференции «Литье по газифицируемым моделям». СПб. 2007. С. 28–32.
Особенности методики подготовки образцов для автоматического анализа карбидной фазы стали Х12Ф1 после цементации в вакууме с применением программного комплекса "Thixomet Pro" / С.Г. Иванов [и др.] // Ползуновский вестник. 2020. № 2. С. 165–168. doi: 10.25712/ASTU.2072-8921.2020.02.031.
Методика пробоподготовки образцов высоколегированных сталей для автоматического анализа карбидной фазы / С.Г. Иванов [и др.]. // Ползуновский вестник. 2020. № 3. С. 102–105. doi: 10.25712/ASTU.2072-8921.2020.03.018.
Kazakov A.A., Ryaboshuk S.V., Lyuboch-ko D.A., Chigintsev L.S. Research on the Origin of Nonmetallic Inclusions in High-Strength Low-Alloy Steel Using Automated Feature Analysis // Microscopy and Microanalysis. 2015. V. 21. № 3. P. 1755–1756.
Kazakov A.A., Kiselev D. Industrial Application of Thixomet // Metallography, Microstructure, and Analysis. 2016. 5. P. 294–301.
Kazakov A.A., Kiselev D. Industrial application of thixomet image analyzer for quantitative description of steel and alloys microstructure // Microscopy and Microanalysis. 2015. V. 21. № 3. P. 457.
Гурьев М.А. Повышение износостойкости деталей машин и инструмента поверхностным легированием при производстве литых изделий : автореф. дис. … канд. техн. наук / Алтайский государственный технический университет им. И.И. Ползунова. Барнаул, 2010. 17 с.
Технология упрочнения стальных изделий в процессе литья / М.А. Гурьев [и др.] // Литейщик России. 2013. № 6. С. 36–38.
Downloads
Published
How to Cite
Issue
Section
License
Copyright (c) 2022 Amantai E. Erbolatov, Mikhail A. Guryev, Sergey G. Ivanov, Artur I. Augstkaln
This work is licensed under a Creative Commons Attribution 4.0 International License.
.
This work is licensed under a 